荷兰DSM PA46 Stanyl 46SF5030 特性:可电镀,含30%玻璃纤维强化,超高阻燃性(0.3mm V-0),超高流动性,壁薄可达到0.4mm。 出色的加工性能、高强度和延展性,以及高结合线强度使其能用于生产最小、最薄且可靠性最高的连接器。与最新一代LCP材料具有相同的流动性,但其壁厚更薄,在多结合线的应用中展现出更优良的机械特性。
PA46 46SF5030 物性表:
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
12000
|
7500
|
MPa
|
ISO 527-2 |
Tensile Stress (Break)
|
170
|
110
|
MPa
|
ISO 527-2 |
Tensile Strain (Break)
|
1.9
|
2.8
|
%
|
ISO 527-2 |
Flexural Modulus
|
11000
|
6800
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
12
|
12
|
kJ/m²
|
|
23°C
|
13
|
13
|
kJ/m²
|
|
Charpy Unnotched Impact Strength (23°C)
|
40
|
40
|
kJ/m²
|
ISO 179/1eU |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
290
|
--
|
°C
|
ISO 75-2/A |
Melting Temperature 2
|
295
|
--
|
°C
|
ISO 11357-3 |
CLTE - Flow
|
0.000020
|
--
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse
|
0.000045
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity
|
> 1.0E+15
|
1.0E+10
|
ohm·cm
|
IEC 60093 |
Electric Strength
|
30
|
20
|
kV/mm
|
IEC 60243-1 |
Comparative Tracking Index
|
225
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flammability Classification
|
IEC 60695-11-10, -20 | |||
0.350 mm
|
V-0
|
--
|
||
1.50 mm
|
V-0
|
--
|